High Tensile Brass Rods Manufacturer

Cw713r Rod, Cw721r Brass Bars, BS 2874/ JIS High Tensile Brass Rods Casting Manufacturers.

JIS 3250H and HT1/HT2 IS 320 High Tensile Brass Rods Suppliers

 

High Tensile Brass Rods
High Tensile Brass Rods
Cw713r Rod
Cw713r Rod
Cw721r Brass Bars
Cw721r Brass Bars

 

Zinc and copper are alloyed to produce brass. The result of their chemistry yields in a highly corrosion resistant alloy. Besides copper and zinc, a High Tensile Brass Rods Manufacturer may use additional elements to alloy brass, thereby increasing its properties, namely its tensile strength. For instance, Cw713r Rod is a high tensile brass alloy. This particular metal has been alloyed with elements like aluminium, manganese and silicon.

The chemistry of this alloy ensures that the resultant JIS 3250H High Tensile Brass Rods Casting tends to be almost as hard as aluminium bronze. However, this alloy tends to be considerably easier to process. Along with achieving high tensile strength, the other important properties of the CW713R HT2 IS 320 High Tensile Brass Rods includes good resistance to corrosion, good wear resistance and machinability. CZ114 or as also referred to as Cw721r Brass Bars, includes alloying elements like aluminium, iron, and manganese. This unique alloying chemistry results in a duplex microstructure in JIS 3250H High Tensile Brass Rods.

Grade CZ114 is well suited for applications involving extraction. Hence, the use of this HT1 IS 320 High Tensile Brass Rods are more often than not seen in marine environments. Since the content of copper in these rods are relatively higher than zinc, the resistance to seawater is characteristically inherent in these components. Along with marine engineering, the BS 2874 High Tensile Brass Rods is in high demand in the oil and gas industry as well.

 

Specification of High Tensile Brass Rods

  • Size: 6 to 60mm
  • Thickness:0 274 mm to 6.35 mm
  • Thickness:4 mm to 150 mm
  • Standard & Material: BS:1001, HT12472, IS:320l, IS 320 HT1 or HT2, BS 2874 CZ114 or CZ115,JIS 3250H C6782 or C6783

HT 12472/ JIS 3250H HT/ HT IS 320/ HT BS 1001 High Tensile Brass Rods Suppliers.

Mechanical & Physical Properties of High Tensile Brass Rods

Condition Size T.S. MPa EL% Min T.S. MPa EL% Min
As manufactured All Size 430 min 20.00% 460 min 20.00%
Cold-worked & Stress 10-40 480 min 12.00% 520 min 12.00%
Relieved 40 above     500 min 15.00%
Chemical Composition of High Tensile Brass Rods

Chemical Requirements HT1 HT2
Copper 56.0 – 60.0% 56.0 – 61.0%
Lead 0.20 to 1.50% 0.50 to 1.50%
Iron 0.20 to 1.25% 0.20 to 1.50%
Tin 0.20 to 1.0% 1.0% max
Aluminum 0.2% max 0.30 to 2%
Manganese 0.25 – 2.0% 0.50-2.0%
Total Imp. 0.50% max 0.50% max
Zinc Remainder Remainder
 