C11000 Electrolytic Tough Pitch Copper Bar
C11000 Electrolytic Tough Pitch Copper Bar

 

Copper is a very versatile metal and can be alloyed with many others to give certain characteristics. One of the primary characteristics of copper is good electrical conductivity. Which is why for applications that have requirements for good electricity flow, manufacturers are very likely to recommend the use of a C11000 Copper Bar. Copper grade C11000 may also be referred to as Electrolytic Tough Pitch.

Being a common grade of copper, the C11000 Electrolytic Tough Pitch (ETP) is a universal component for electrical applications. With a minimum conductivity rating of 100% IACS, the purity value of the C11000 Electrolytic Tough Pitch Copper is required to stand at 99.9%. Though the purity needs to be kept to a minimum of 99.9%, it is not unheard of that the Electrolytic Tough Pitch Casting contains some trace quantity of oxygen in its chemistry.

Typically, it is expected that this pure grade has an oxygen content ranging between 0.02% to 0.04%. Usually, the use of C11000 Copper Rod involves the most demanding electrical applications including the likes of the transmission of power as well as signals.

 

Specification of C11000 Copper Bar

Standard & Material
CDA 110 ETP, ASTM B124, ASTM B152, ASTM B187, ASTM B188, ASTM B272
HOLLOW RODS
Min Bore Size 20 mm and Max OD 100 mm
ROUND RODS
8mm To 100 mm
HEX
10mm To 60mm
SQUARE
10mm To 60mm
FLAT
10mm Min Thickness and max Width 120mm
BILLETS
Up to 200 mm
INGOTS
As per Specification
Applications of C11000 Copper Bar

  • Architectural Industry
  • Antimicrobial Applications
  • Electrical Industry
  • Telecommunications Industry
Equivelent Specifications of C11000 Copper Bar

 

End Product
Specification
Bar
ASME SB133, ASTM B152, SAE J461, J463
Bar, Bus
ASTM B187
Bar, Forging
ASTM B124
Rod
ASME SB133, MILITARY MIL-C-12166, SAE J461, J463
Rod, Bus
ASTM B187

 

Chemical Composition of C11000 Copper Bar

Element
Content (%)
Cu
99.90
Physical Properties of C11000 Copper Bar

Properties
Metric
Imperial
Density
8.89 g/cm3
0.322 lb/in3
Melting point
1065 – 1083°C
1949°F
Mechanical Properties of C11000 Copper Bar

Properties
Metric
Imperial
Hardness, Rockwell F (hard temper)
80.0
80.0
Poisson’s ratio
0.34
0.34
Elastic modulus
115 – 117 GPa
16969 ksi
Fabrication of C11000 Copper Bar

Joining Technique
Suitability
Brazing
Good
Butt Weld
Good
Capacity for Being Cold Worked
Excellent
Capacity for Being Hot Formed
Excellent
Coated Metal Arc Welding
Not Recommended
Forgeability Rating
65
Gas Sheilded Arc Welding
Fair
Machinability rating
20
Oxyacetylene Welding
Not Recommended
Seam Weld
Not Recommended
Soldering
Excellent
Spot Weld
Not Recommended