SAE 1015 Round Bar

Steels components such as SAE 1015 Round Bar with only carbon as their major alloying element are referred to as carbon steels. According to the ASTM 1015 Steel Chemical composition, this carbon steel grade contains traces contents of both silicon and manganese.

View SAE 1015 round bar price. largest AISI 1015 Round Bar, SAE 1015 rods manufacturer

SAE 1015 Round Bar
SAE 1015 Round Bar
AISI 1015 Rods
AISI 1015 Rods
1015 Steel Cold Drawn Bar
1015 Steel Cold Drawn Bar

 

Check SAE 1015 round bar weight, Suppliers of AISI 1015 steel cold drawn bar, 1015 Carbon Steel Rods

Apart from these two alloyants, the carbon steel hot rolled round bar 1015 also contain trace quantities of elements like aluminium, copper, nickel, molybdenum, and chromium. Carbon steel based 1015 Bearing steel rod could be used in applications which require low tensile strength along with good resistance to wear and hard surfaces. Per specification ASTM A29, the carbon based 1015 Steel Round Bar is to not only undergo a Heat and product analysis but the chemistry also needs to conform to its specification.

Furthermore, the material i.e. ASTM A29 1015 Round bar must not only undergo a grain size test but the bar needs to conform to the specified grain size requirement. The ASTM A29 specification also mentions that mechanical tests have to be performed on the aisi 1015 steel cold drawn bar test specimens. The sae 1015 material properties of this engineering carbon steek grade alloy include its superior workability and machinability. Welding of this grade 1015 Carbon Steel Rods could be carried out by using all normal fusion methods. One such method is using low-carbon electrodes, which are often preferred by users of the 1015 Round Bar. These sae 1015 rods are supplied in any one of the following condition i.e. – normalized, hot-rolled, cold-worked or annealed.

 

Our Manufacturing Size range of 1015 Round Steel Bars


16mm, 18mm, 20mm, 22mm, 23.5mm, 24mm, 25mm, 26mm, 27mm, 28mm, 30mm, 32mm, 34mm, 35mm, 36mm, 37mm, 38mm, 40mm, 42mm, 45mm, 46.5mm, 47mm, 50mm, 51mm,53mm, 56mm, 60mm, 63mm, 65mm, 70mm, 75mm, 78mm, 80mm, 85mm, 90mm, 95mm, 100mm, 105mm, 110mm, 115mm, 120mm, 125mm, 130mm.

 

Material Equivalent grades of 1015 round bars:

C15E, C15, CK15

 

Following Aditional Grades We Manufacture except 1015 Round Bars:

MS, SAE 1018, IS 2062, A105, SAE 1008, SAE 1010, SAE 1015, C15, C18, C20, 1020, C22, 1022, C25, 1025, C30, 1030, C35, 1035, 35C8, S35C, C40, 1040, C45, 45C8, 1045, CK45, C50, 1050, C55, 55C8, 1055, C60, 1060, C70, 41Cr4, 40Cr4, 40Cr1, En18, En18D, SAE 1541, SAE 1536, 37Mn2, 37C15, En15, SAE 1141, LF2, EN19, SAE 4140, 42CrMo4, EN24, EN31, SAE 52100, 20MnCr5, 8620, EN1A, EN8, EN8D, EN9, ST 52.3, EN42, En353, SS 410, SS 202, SS 304, SS 316 and other grades as per customer requirement.

 

See SAE 1015 material properties, Most Reliable 1015 Steel Round Bar Exporter

 

Mechanical Characteristics of 1015 Round Bar

Properties
Metric
Imperial
Tensile strength
385 MPa
55800 psi
Yield strength
325 MPa
47100 psi
Bulk modulus (typical for steel)
140 GPa
20300 ksi
Shear modulus (typical for steel)
80.0 GPa
11600 ksi
Elastic modulus
190-210 GPa
27557-30458 ksi
Poisson’s ratio
0.27-0.30
0.27-0.30
Elongation at break (In 50 mm)
18.00%
18.00%
Reduction of area
40.00%
40.00%
Hardness, Brinell
111
111
Hardness, Knoop (converted from Brinell hardness)
129
129
Hardness, Rockwell B (converted from Brinell hardness)
64
64
Hardness, Vickers (converted from Brinell hardness)
115
115
Machinability (based on AISI 1212 steel as 100 machinability. The machinability of Group I bar, rod, and wire products can be improved by cold drawing.)
60
60

 

Physical Properties of 1015 Round Bar

Properties
Metric
Imperial
Density
7.87 g/cc
0.284 lb/in³

 

Looking for ASTM A29 1015 Round bar, 1015 Bearing steel rod manufacturer in India ?
Thermal Properties of 1015 Round Bar

Properties
Metric
Imperial
Thermal expansion co-efficient (@0.000-100°C/32.0-212°F)
11.9 µm/m°C
6.61 µin/in°F
Thermal conductivity (estimated based on similar materials)
51.9 W/mK
360 BTU in/hr.ft².°F

 

Relate Steel Type

Steel Type
Standard
Country Code
C(%)
Si(%)
Mn(%)
P(%)
S(%)
S15C
3828
CNS
0.13-0.18
0.15-0.35
0.3-0.6
≦0.03
≦0.035
15
699
GB
0.12-0.18
0.17-0.37
0.35-0.65
≦0.035
≦0.035
S15C
G4051
JIS
0.13-0.18
0.15-0.35
0.3-0.6
≦0.03
≦0.035
1015
AISI
0.13-0.18
0.15-0.35
0.3-0.6
≦0.04
≦0.05
C15
17210
DIN
0.12-0.18
0.15-0.35
0.3-0.8
≦0.045
≦0.045
Ck15
17210
DIN
0.12-0.18
0.15-0.35
0.3-0.6
≦0.035
≦0.035
Cm15
17210
DIN
0.12-0.18
0.15-0.35
0.3-0.6
≦0.035
0.020-0.035

 

Find here ASTM 1015 Steel Chemical composition, PED Approved carbon steel hot rolled round bar 1015 Suppliers
Chemical Composition Table of 1015 Round Bar

Element
Content (%)
Iron, Fe
99.13-99.57
Carbon, C
0.13-0.18
Manganese, Mn
0.30-0.60
Sulfur, S
≤ 0.050
Phosphorous, P
≤ 0.040

 